ADWEL 1630B
| Property | Value | Unit | Method |
|---|---|---|---|
| Appearance | Milky white | test2 | |
| Weight Solids | 50±1 | % | WHPU/T011-571-2017 (5cm,150°C,20min) |
| pH | 6.0 - 9.0 | GB / T 14518-1993 | |
| Viscosity | 500 - 4000 | mPa.s | GB/T 2794-2013 (Brookfield,LV,63#/12rpm,25℃) |
| Density | 1.04 - 1.09 | g/cm3 | GB/T 4472-2011 |
| Activated Temperature | 60 - 70 | °C | SP-WHSM-07-1017 |
| MFFT | 10 - 15 | °C | SP-WHSM-07-1030 |
| *These properties are typical but do not constitute specifications. |
|||
- Description
- Additional information
- Reviews (0)
Description
WHAT IS IT
Raw material for the formulation of heat activated adhesives in footwear industries
WHY USE IT
- Outstanding initial tacky property
- Excellent bonding strength
- Excellent brushability
- Excellent heat/water resistance
- Bonding strength, heat and water resistance can be enhanced by adding an appropriate amount of water dispersible polyisocyanate hardener like Aquolin 161.
| Solvent | <1% Acetone |
|---|---|
| Bioside | CMIT/MIT 3:1 49ppm MIT 100ppm |
Aqueous Polyurethane Dispersion Characteristic Data*
Additional information
| Industry | Construction |
|---|
Be the first to review “ADWEL 1630B”
Related Products
-
Aqueous Polyurethane Dispersion, Footwear
Wanhua
ADWEL 1654
Aqueous Polyurethane Dispersion
Industry : -
3D lamination, Automotive Interior, Footwear, Hydrophilically Modified Polyisocyanate, Hydrophilically Modified Polyisocyanate, Hydrophilically Modified Polyisocyanate
Wanhua
AQUOLIN 166
Hydrophilically Modified Polyisocyanate
Industry :
WHAT IS IT
Raw material for the formulation of heat activated adhesives in footwear industries
WHY USE IT
- Outstanding initial tacky property
- Excellent bonding strength
- Excellent brushability
- Excellent heat/water resistance
- Bonding strength, heat and water resistance can be enhanced by adding an appropriate amount of water dispersible polyisocyanate hardener like Aquolin 161.
| Solvent | <1% Acetone |
|---|---|
| Bioside | CMIT/MIT 3:1 49ppm MIT 100ppm |
Aqueous Polyurethane Dispersion Characteristic Data*
[get_product_name_table]
| Property | Value | Unit | Method |
|---|---|---|---|
| Appearance | Milky white | test2 | |
| Weight Solids | 50±1 | % | WHPU/T011-571-2017 (5cm,150°C,20min) |
| pH | 6.0 - 9.0 | GB / T 14518-1993 | |
| Viscosity | 500 - 4000 | mPa.s | GB/T 2794-2013 (Brookfield,LV,63#/12rpm,25℃) |
| Density | 1.04 - 1.09 | g/cm3 | GB/T 4472-2011 |
| Activated Temperature | 60 - 70 | °C | SP-WHSM-07-1017 |
| MFFT | 10 - 15 | °C | SP-WHSM-07-1030 |
| *These properties are typical but do not constitute specifications. |
|||
Reviews
There are no reviews yet.