AQUOLIN 166
| Property | Value | Unit | Method |
|---|---|---|---|
| Appearance | Transparent to light yellow liquid | ||
| Weight Solids | ≥99.8 | % | WHPU/T011-571-2017 (5cm,105°C,60min) |
| NCO content | 21.5-22.5 | WT% | GB 12009.4-2016 |
| Viscosity(25°C) | 700 - 1700 | mPa.s | GB/T 2794-2013 (Brookfield,LV,63#/30rpm,25℃) |
| Color APHA | <60 | GB/T 1722-1992 |
|
| HDI monomer content | ≤0.2 | WT% | GB/T 18446-2009 |
| Flash point | ~226 | °C | GB/T 5208-2008 |
| Density | ~1.16 | g/cm3 | GB/T 4472-2011 |
| *Property values represent typical results only and are not to be considered as specifications, subject to specific COA | |||
- Description
- Additional information
- Reviews (0)
Description
Description
WHAT IS IT
It is a hydrophilically modified polyisocyanate. It can be used with various hydroxyl functionalized dispersions for 2k solutions.
WHY USE IT
- High functionality with low viscosity
- Good dispersibility
- Long pot life
- An appropriate amount of Aquolin® 166 in waterborne polyurethane adhesive can enhance the bonding strength, heat resistance and hydrolysis resistance significantly.
Hydrophilically Modified Polyisocyanate Characteristic Data*
Additional information
Additional information
| Industry | Automotive Interior |
|---|---|
| Suppliers | Wanhua |
Reviews (0)
Be the first to review “AQUOLIN 166”
Related Products
-
Aqueous Polyurethane Dispersion, Footwear
Wanhua
ADWEL 1630B
Aqueous Polyurethane Dispersion
Industry : -
Aqueous Polyurethane Dispersion, Automotive Interior
Wanhua
ADWEL 1633
Aqueous Polyurethane Dispersion
Industry : -
Aqueous Polyurethane Dispersion, Footwear
Wanhua
ADWEL 1654
Aqueous Polyurethane Dispersion
Industry :
WHAT IS IT
It is a hydrophilically modified polyisocyanate. It can be used with various hydroxyl functionalized dispersions for 2k solutions.
WHY USE IT
- High functionality with low viscosity
- Good dispersibility
- Long pot life
- An appropriate amount of Aquolin® 166 in waterborne polyurethane adhesive can enhance the bonding strength, heat resistance and hydrolysis resistance significantly.
Hydrophilically Modified Polyisocyanate Characteristic Data*
[get_product_name_table]
| Property | Value | Unit | Method |
|---|---|---|---|
| Appearance | Transparent to light yellow liquid | ||
| Weight Solids | ≥99.8 | % | WHPU/T011-571-2017 (5cm,105°C,60min) |
| NCO content | 21.5-22.5 | WT% | GB 12009.4-2016 |
| Viscosity(25°C) | 700 - 1700 | mPa.s | GB/T 2794-2013 (Brookfield,LV,63#/30rpm,25℃) |
| Color APHA | <60 | GB/T 1722-1992 |
|
| HDI monomer content | ≤0.2 | WT% | GB/T 18446-2009 |
| Flash point | ~226 | °C | GB/T 5208-2008 |
| Density | ~1.16 | g/cm3 | GB/T 4472-2011 |
| *Property values represent typical results only and are not to be considered as specifications, subject to specific COA | |||