CELVOLIT 1498
| Property | Method | Unit | Typical value |
|---|---|---|---|
| Solid content (130 °C, 30min) | ISO 3251 | % | 54.5 ~ 56.5 |
| Brookfield viscosity(Spindle nr 4/20rpm/25˚C, BVF RVT) | ISO 2555 | mPa.s | 3000-4500 |
| pH value | ISO 976 | 4.0 ~ 5.0 |
|
| Particle size | μm | approx. 1.2 |
|
| Minimum film forming temperature (MFFT) | ISO 2115 | °C | Approx. 0 |
| Glass transition temperature (Heat rate 10˚C/min, on set point) | ISO 16805 | °C | Approx. 3 |
| Glass transition temperature (Heat rate 10˚C/min, middle point) | ISO 16805 | °C | Approx. 6 |
| Appearance of polymer film | Slightly opaque, soft film. |
||
- Description
- Additional information
- Reviews (0)
Description
WHAT IS IT
It is an un plasticized copolymer emulsion of Vinyl acetate and ethylene.
WHY USE IT
- High wet tack
- Fast setting
- It provides adhesion to a wide variety of porous and nonporous substrates with a strong, yet permanently flexible adhesive bond, also with excellent heat resistance.
- When Celvolit®1498 (SG) is dried at temperatures above 0˚C, the dispersion forms a slightly opaque, soft film without the addition of solvents or plasticizers.
- Is compatible with a variety of plasticizers, solvents, fillers and other modifiers
Copolymer Emulsion of Vinyl Acetate and Ethylene Characteristic Data*
Additional information
| Industry | Construction |
|---|
Be the first to review “CELVOLIT 1498”
Related Products
-
Adhesives, Copolymer Emulsion of Vinyl Acetate and Ethylene, Copolymer Emulsion of Vinyl Acetate and Ethylene, Copolymer Emulsion of Vinyl Acetate and Ethylene, Copolymer Emulsion of Vinyl Acetate and Ethylene, Packaging, Paper, Wood
Celanese
CELVOLIT 1488
Copolymer Emulsion of Vinyl Acetate and Ethylene
-
Converting Adhesives, Copolymer Emulsion of Vinyl Acetate and Ethylene, Copolymer Emulsion of Vinyl Acetate and Ethylene, Paper
Celanese
CELVOLIT 1499
Copolymer Emulsion of Vinyl Acetate and Ethylene
Industry : -
Adhesives, Hydrophobically Modified Polyvinyl Alcohol, Hydrophobically Modified Polyvinyl Alcohol, Hydrophobically Modified Polyvinyl Alcohol, Paper, Wood
Kuraray
EXCEVAL RS-2717
Hydrophobically Modified Polyvinyl Alcohol
-
Adhesives, Construction, Packaging, Paper, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Textile
Kuraray
POVAL 27- 96
Polyvinyl Alcohol
Industry : -
Adhesives, Construction, Packaging, Paper, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Textile
Kuraray
POVAL 49-88
Polyvinyl Alcohol
Industry :
CELVOLIT 1498
CELVOLIT 1498
Copolymer Emulsion of Vinyl Acetate and Ethylene
WHAT IS IT
It is an un plasticized copolymer emulsion of Vinyl acetate and ethylene.
WHY USE IT
- High wet tack
- Fast setting
- It provides adhesion to a wide variety of porous and nonporous substrates with a strong, yet permanently flexible adhesive bond, also with excellent heat resistance.
- When Celvolit®1498 (SG) is dried at temperatures above 0˚C, the dispersion forms a slightly opaque, soft film without the addition of solvents or plasticizers.
- Is compatible with a variety of plasticizers, solvents, fillers and other modifiers
Copolymer Emulsion of Vinyl Acetate and Ethylene Characteristic Data*
[get_product_name_table]
| Property | Method | Unit | Typical value |
|---|---|---|---|
| Solid content (130 °C, 30min) | ISO 3251 | % | 54.5 ~ 56.5 |
| Brookfield viscosity(Spindle nr 4/20rpm/25˚C, BVF RVT) | ISO 2555 | mPa.s | 3000-4500 |
| pH value | ISO 976 | 4.0 ~ 5.0 |
|
| Particle size | μm | approx. 1.2 |
|
| Minimum film forming temperature (MFFT) | ISO 2115 | °C | Approx. 0 |
| Glass transition temperature (Heat rate 10˚C/min, on set point) | ISO 16805 | °C | Approx. 3 |
| Glass transition temperature (Heat rate 10˚C/min, middle point) | ISO 16805 | °C | Approx. 6 |
| Appearance of polymer film | Slightly opaque, soft film. |
||