CELVOLIT 1499
| Specification and Property | Method | Unit | Typical value |
|---|---|---|---|
| Solid content (130 °C, 30min) | ISO 3251 | % | 54.5 ~ 56.5 |
| Brookfield viscosity(4#60,25˚C, BVF RVT) | ISO 2555 | mPa.s | 1,500-2,500* |
| pH value | ISO 976 | 4.0 ~ 5.0 |
|
| Particle size | μm | approx. 1.0 |
|
| Minimum film forming temperature (MFFT) | ISO 2115 | °C | Approx. 0 |
| Glass transition temperature (Heat rate 10˚C/min, on set point) | ISO 16805 | °C | Approx. 2 |
| Glass transition temperature (Heat rate 10˚C/min, middle point) | ISO 16805 | °C | Approx. 6 |
| Appearance of polymer film | Slightly opaque, soft film. |
||
| *Temporary specification. |
|||
- Description
- Additional information
- Reviews (0)
Description
WHAT IS IT
It is an un plasticized copolymer emulsion of Vinyl acetate and ethylene.
WHY USE IT
- High wet tack.
- Fast setting speed.
- It provides adhesion to a wide variety of porous and nonporous substrates with a strong, yet permanently flexible adhesive bond, also with excellent heat resistance.
- When Celvolit® 1499 (SG) is dried at temperatures above 0˚C, the dispersion forms a slightly opaque, soft film without the addition of solvents or plasticizers.
- It is suitable for manual, roller, wheel and nozzle application.
- It is compatible with a variety of plasticizers, solvents, fillers and other modifiers.
Copolymer Emulsion of Vinyl Acetate and Ethylene Characteristic Data*
Additional information
| Industry | Construction |
|---|
Be the first to review “CELVOLIT 1499”
Related Products
-
Adhesives, Copolymer Emulsion of Vinyl Acetate and Ethylene, Copolymer Emulsion of Vinyl Acetate and Ethylene, Copolymer Emulsion of Vinyl Acetate and Ethylene, Copolymer Emulsion of Vinyl Acetate and Ethylene, Packaging, Paper, Wood
Celanese
CELVOLIT 1488
Copolymer Emulsion of Vinyl Acetate and Ethylene
-
Converting Adhesives, Copolymer Emulsion of Vinyl Acetate and Ethylene, Copolymer Emulsion of Vinyl Acetate and Ethylene, Paper
Celanese
CELVOLIT 1498
Copolymer Emulsion of Vinyl Acetate and Ethylene
Industry : -
Adhesives, Construction, Packaging, Paper, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Textile
Kuraray
POLYSIZER -173
Polyvinyl Alcohol
Industry : -
Adhesives, Construction, Packaging, Paper, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Textile
Kuraray
POVAL 22-88
Polyvinyl Alcohol
Industry : -
Adhesives, Construction, Packaging, Paper, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Textile
Kuraray
POVAL 95-88
Polyvinyl Alcohol
Industry :
CELVOLIT 1499
CELVOLIT 1499
Copolymer Emulsion of Vinyl Acetate and Ethylene
WHAT IS IT
It is an un plasticized copolymer emulsion of Vinyl acetate and ethylene.
WHY USE IT
- High wet tack.
- Fast setting speed.
- It provides adhesion to a wide variety of porous and nonporous substrates with a strong, yet permanently flexible adhesive bond, also with excellent heat resistance.
- When Celvolit® 1499 (SG) is dried at temperatures above 0˚C, the dispersion forms a slightly opaque, soft film without the addition of solvents or plasticizers.
- It is suitable for manual, roller, wheel and nozzle application.
- It is compatible with a variety of plasticizers, solvents, fillers and other modifiers.
Copolymer Emulsion of Vinyl Acetate and Ethylene Characteristic Data*
[get_product_name_table]
| Specification and Property | Method | Unit | Typical value |
|---|---|---|---|
| Solid content (130 °C, 30min) | ISO 3251 | % | 54.5 ~ 56.5 |
| Brookfield viscosity(4#60,25˚C, BVF RVT) | ISO 2555 | mPa.s | 1,500-2,500* |
| pH value | ISO 976 | 4.0 ~ 5.0 |
|
| Particle size | μm | approx. 1.0 |
|
| Minimum film forming temperature (MFFT) | ISO 2115 | °C | Approx. 0 |
| Glass transition temperature (Heat rate 10˚C/min, on set point) | ISO 16805 | °C | Approx. 2 |
| Glass transition temperature (Heat rate 10˚C/min, middle point) | ISO 16805 | °C | Approx. 6 |
| Appearance of polymer film | Slightly opaque, soft film. |
||
| *Temporary specification. |
|||
Reviews
There are no reviews yet.