CELVOLIT 1499

Specification and PropertyMethodUnitTypical value
Solid content (130 °C, 30min)​ISO 3251%54.5 ~ 56.5
Brookfield viscosity(4#60,25˚C, BVF RVT)​ISO 2555mPa.s1,500-2,500*​
pH value​ISO 9764.0 ~ 5.0​
Particle size​
μmapprox. 1.0
Minimum film forming temperature (MFFT)​ISO 2115°CApprox. 0
Glass transition temperature (Heat rate 10˚C/min, on set point)​
ISO 16805
°CApprox. 2
Glass transition temperature (Heat rate 10˚C/min, middle point)​
ISO 16805
°CApprox. 6
Appearance of polymer film​
Slightly opaque, soft film.​

*Temporary specification.​

Description

WHAT IS IT

It is an un plasticized copolymer emulsion of Vinyl acetate and ethylene.​

WHY USE IT

  • High wet tack.​​
  • Fast setting speed.​​
  • It provides adhesion to a wide variety of porous and nonporous substrates with a strong, yet permanently flexible adhesive bond, also with excellent heat resistance.​​
  • When Celvolit® 1499 (SG) is dried at temperatures above 0˚C, the dispersion forms a slightly opaque, soft film without the addition of solvents or plasticizers.​
  • It is suitable for manual, roller, wheel and nozzle application.​​
  • It is compatible with a variety of plasticizers, solvents, fillers and other modifiers.​


Copolymer Emulsion of Vinyl Acetate and Ethylene Characteristic Data*

Additional information

Industry

Construction

Reviews

There are no reviews yet.


Be the first to review “CELVOLIT 1499”

CELVOLIT 1499

Copolymer Emulsion of Vinyl Acetate and Ethylene

CELVOLIT 1499

CELVOLIT 1499

Copolymer Emulsion of Vinyl Acetate and Ethylene

WHAT IS IT

It is an un plasticized copolymer emulsion of Vinyl acetate and ethylene.​

WHY USE IT

  • High wet tack.​​
  • Fast setting speed.​​
  • It provides adhesion to a wide variety of porous and nonporous substrates with a strong, yet permanently flexible adhesive bond, also with excellent heat resistance.​​
  • When Celvolit® 1499 (SG) is dried at temperatures above 0˚C, the dispersion forms a slightly opaque, soft film without the addition of solvents or plasticizers.​
  • It is suitable for manual, roller, wheel and nozzle application.​​
  • It is compatible with a variety of plasticizers, solvents, fillers and other modifiers.​


Copolymer Emulsion of Vinyl Acetate and Ethylene Characteristic Data*

[get_product_name_table]
Specification and PropertyMethodUnitTypical value
Solid content (130 °C, 30min)​ISO 3251%54.5 ~ 56.5
Brookfield viscosity(4#60,25˚C, BVF RVT)​ISO 2555mPa.s1,500-2,500*​
pH value​ISO 9764.0 ~ 5.0​
Particle size​
μmapprox. 1.0
Minimum film forming temperature (MFFT)​ISO 2115°CApprox. 0
Glass transition temperature (Heat rate 10˚C/min, on set point)​
ISO 16805
°CApprox. 2
Glass transition temperature (Heat rate 10˚C/min, middle point)​
ISO 16805
°CApprox. 6
Appearance of polymer film​
Slightly opaque, soft film.​

*Temporary specification.​