CELVOLIT 1498
| Property | Method | Unit | Typical value |
|---|---|---|---|
| Solid content (130 °C, 30min) | ISO 3251 | % | 54.5 ~ 56.5 |
| Brookfield viscosity(Spindle nr 4/20rpm/25˚C, BVF RVT) | ISO 2555 | mPa.s | 3000-4500 |
| pH value | ISO 976 | 4.0 ~ 5.0 |
|
| Particle size | μm | approx. 1.2 |
|
| Minimum film forming temperature (MFFT) | ISO 2115 | °C | Approx. 0 |
| Glass transition temperature (Heat rate 10˚C/min, on set point) | ISO 16805 | °C | Approx. 3 |
| Glass transition temperature (Heat rate 10˚C/min, middle point) | ISO 16805 | °C | Approx. 6 |
| Appearance of polymer film | Slightly opaque, soft film. |
||
- Description
- Additional information
- Reviews (0)
Description
WHAT IS IT
It is an un plasticized copolymer emulsion of Vinyl acetate and ethylene.
WHY USE IT
- High wet tack
- Fast setting
- It provides adhesion to a wide variety of porous and nonporous substrates with a strong, yet permanently flexible adhesive bond, also with excellent heat resistance.
- When Celvolit®1498 (SG) is dried at temperatures above 0˚C, the dispersion forms a slightly opaque, soft film without the addition of solvents or plasticizers.
- Is compatible with a variety of plasticizers, solvents, fillers and other modifiers
Copolymer Emulsion of Vinyl Acetate and Ethylene Characteristic Data*
Additional information
| Industry | Construction |
|---|
Be the first to review “CELVOLIT 1498”
Related Products
-
Converting Adhesives, Copolymer Emulsion of Vinyl Acetate and Ethylene, Copolymer Emulsion of Vinyl Acetate and Ethylene, Paper
Celanese
CELVOLIT 1499
Copolymer Emulsion of Vinyl Acetate and Ethylene
Industry : -
Adhesives, Hydrophobically Modified Polyvinyl Alcohol, Hydrophobically Modified Polyvinyl Alcohol, Hydrophobically Modified Polyvinyl Alcohol, Paper, Wood
Kuraray
EXCEVAL RS-1717
Hydrophobically Modified Polyvinyl Alcohol
-
Adhesives, Construction, Packaging, Paper, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Textile
Kuraray
POLYSIZER -173
Polyvinyl Alcohol
Industry : -
Adhesives, Construction, Packaging, Paper, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Textile
Kuraray
POVAL 3-88
Polyvinyl Alcohol
Industry : -
Adhesives, Construction, Packaging, Paper, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Polyvinyl Alcohol, Textile
Kuraray
POVAL 30-88 DB
Polyvinyl Alcohol
Industry :
CELVOLIT 1498
CELVOLIT 1498
Copolymer Emulsion of Vinyl Acetate and Ethylene
WHAT IS IT
It is an un plasticized copolymer emulsion of Vinyl acetate and ethylene.
WHY USE IT
- High wet tack
- Fast setting
- It provides adhesion to a wide variety of porous and nonporous substrates with a strong, yet permanently flexible adhesive bond, also with excellent heat resistance.
- When Celvolit®1498 (SG) is dried at temperatures above 0˚C, the dispersion forms a slightly opaque, soft film without the addition of solvents or plasticizers.
- Is compatible with a variety of plasticizers, solvents, fillers and other modifiers
Copolymer Emulsion of Vinyl Acetate and Ethylene Characteristic Data*
[get_product_name_table]
| Property | Method | Unit | Typical value |
|---|---|---|---|
| Solid content (130 °C, 30min) | ISO 3251 | % | 54.5 ~ 56.5 |
| Brookfield viscosity(Spindle nr 4/20rpm/25˚C, BVF RVT) | ISO 2555 | mPa.s | 3000-4500 |
| pH value | ISO 976 | 4.0 ~ 5.0 |
|
| Particle size | μm | approx. 1.2 |
|
| Minimum film forming temperature (MFFT) | ISO 2115 | °C | Approx. 0 |
| Glass transition temperature (Heat rate 10˚C/min, on set point) | ISO 16805 | °C | Approx. 3 |
| Glass transition temperature (Heat rate 10˚C/min, middle point) | ISO 16805 | °C | Approx. 6 |
| Appearance of polymer film | Slightly opaque, soft film. |
||